Step 1: define the real design envelope

Record design pressure, 設計温度, operating range, upset conditions, process medium, corrosion allowance, cyclic duty and expected service life. High-temperature selection is not a single-temperature exercise. Long-term creep exposure, thermal transients, 酸化, hydrogen damage and corrosion under insulation may control different parts of the decision.

The adopted piping code, client specification and line class establish the allowable material route. Published marketing temperature ranges are not a substitute for the code’s allowable stress data or the flange standard’s pressure-temperature tables.

Step 2: select a compatible material system

Match the flange to the adjoining pipe, 継手, バルブ本体, weld metal and bolting strategy. F11, F22 and F91 each belong to a different metallurgical system. A flange with higher nominal strength can introduce mismatched welding, thermal expansion or heat-treatment requirements if used outside its intended line class.

Step 3: rate the flange and design the joint

Use the applicable ASME standard and adopted edition to determine the pressure-temperature rating for the exact material group and class. クラス 600 does not mean 600 psi, とクラス 900 does not mean 900 psi. Available pressure changes with material and temperature.

Then select flange type, 直面している, gasket and bolting as one joint. Weld neck flanges are commonly used for critical high-temperature lines because the butt-welded hub provides a gradual transition. The bore and weld preparation must match the ordered pipe wall. RF versus RTJ selection depends on the equipment connection, gasket standard, service and project philosophy; the two facings are not field-interchangeable.

Step 4: lock in fabrication and quality controls

Before manufacturing, define the required forging route, 熱処理, test frequency, 硬度限界, PMI coverage, surface examination, ultrasonic examination, dimensional inspection and certificate type. The order should also state whether third-party inspection or hold points apply.

For welded systems, align the flange grade with the qualified WPS, 予熱, interpass controls, フィラーメタルとPWHT. 学年 91 work deserves particular discipline because composition verification alone cannot confirm a correct microstructure. Complete traceability from raw material heat to final marking is essential for every grade.